Abstract
Gold nanoparticles dispersed inside the pores of monolithic mesoporous silica were prepared by soaking the silica in a gold (III) ion solution and subsequent ultrasound irradiation. The formation process of gold nanoparticles in the pores of mesoporous silica was investigated based on optical measurements of wrapped and naked soaked silica after ultrasonic irradiation, and the reduction rate effect in solution and pre-soaking effect. It has been shown that acoustic cavitation cannot occur in nano-sized pores. The gold nanoparticles in silica are not formed in situ within the pores but produced mainly by diffusion of the gold clusters formed in the solution during irradiation into the pores. The radicals formed in solution are exhausted before entering the pores of silica. There exists a critical reduction rate in solution, at which the yield of gold nanoparticles in silica reaches a maximum, and above which there is a decrease in the yield. This is attributed to too quick a growth or aggregation of gold clusters formed in solution before diffusion into the pores of silica.
Export citation and abstract BibTeX RIS