Field-induced transitions in single crystals of TbCu4Ag and GdCu4Ag

, , , , , , , and

Published under licence by IOP Publishing Ltd
, , Citation Y Adachi et al 2006 J. Phys.: Conf. Ser. 51 55 DOI 10.1088/1742-6596/51/1/010

Download Article PDF

Article metrics

259 Total downloads

Share this article

Article and author information

Author affiliations

1 Faculty of Engineering, Yamagata University, Yonezawa 992-8510, Japan

2 Faculty of Engineering, Kyushu Institute of Technology, Kitakyushu 804-8550, Japan

3 IMR, Tohoku University, Sendai 980-8577, Japan

4 Department of Physics, Faculty of Science, Tohoku University, Sendai 980-8578, Japan

5 Faculty of Engineering, Kyushu University, Fukuoka 812-8581, Japan

Buy this article in print

Journal RSS
Sign up for new issue notifications
1742-6596/51/1/55

Abstract

Measurements of magnetization were carried out for single crystals of TbCu4Ag and GdCu4Ag under magnetic field up to 18 T at temperatures of 1.7, 3.0 and 4.2 K. At 4.2 K, two stepped field-induced transitions were observed in magnetizing process along all the [111], [110] and [100] directions. At 1.7 K four stepped transitions were observed only along the [100] direction. For GdCu4Ag unusual increase of magnetization was observed in high field magnetization process.