Fabrication of mandible fracture plate by indirect additive manufacturing

Bone fracture is a serious skeletal injury due to accidents and fragility of the bones at a certain age. In order to accelerate fracture healing process, fracture bone plate is use to hold the fracture segment for more stability. The purpose of this study is to fabricate mandibular fracture plate by using indirect additive manufacturing methods in order to reduce time taken during bending and shaping the fracture fixation plate that conform to the anatomy of the fractured bone site. The design and analysis of the plates are performed using CATIA and ANSYS software. The 3D-CAD data were sent to an additive manufacturing machine (fused filament fabricated) to generate master pattern using PLA and the mould were fabricated using Plaster of Paris. A melt ZAMAK 3 was poured directly into the moulds, and left it until completely harden. 3point bending test was performed on the prototype plate using universal testing machine. Stress-strain curve shows the graph exhibited a linear relationship of stress-strain up to a strain value of 0.001. Specimens give a maximum yielding stress and then break before the conventional deflection. Since the maximum flexural stress and the breaking stress are far apart with a plateau stating at strain value of 0.003mm/mm in most specimens, the specimen's failure types are considered plastic failure mode. The average thickness and width are 1.65mm and 2.18mm respectively. The flexural modulus and flexural strength are 189.5GPa and 518.1MPa, respectively.