Bone fracture plates are usually made from steel or titanium, which are much stiffer than cortical bone. This may cause bone 'stress shielding' (i.e. bone resorption leading to plate loosening) and delayed fracture healing (i.e. fracture motion is less than needed to stimulate callus formation at the fracture). Thus, the authors previously designed, fabricated, and mechanically tested novel 'hybrid' composites made from inorganic and organic materials as potential bone fracture plates that are more flexible to reduce these negative effects. This is the first study to measure the cytotoxicity of these composites via the survival of rat cells. Cubes of carbon fiber/flax fiber/epoxy and glass fiber/flax fiber/epoxy had better cell survival vs. Kevlar fiber/flax fiber/epoxy (57% and 58% vs. 50%). Layers and powders made of carbon fiber/epoxy and glass fiber/epoxy had higher cell survival than Kevlar fiber/epoxy (96%–100% and 100% vs. 39%–90%). The presence of flax fibers usually decreased cell survival. Thus, carbon and glass fiber composites (with or without flax fibers), but not Kevlar fiber composites (with or without flax fibers), may potentially be used for bone fracture plates.
ISSN: 1748-605X
Biomedical Materials publishes original research findings and critical reviews that contribute to our knowledge about the composition, properties, and performance of materials for all applications relevant to human healthcare.
Open all abstracts, in this tab
Aurelia Bihari et al 2024 Biomed. Mater. 19 041001
Yibo Yang et al 2024 Biomed. Mater. 19 045004
During the process of malignant tumor treatment, photodynamic therapy (PDT) exerts poor efficacy due to the hypoxic environment of the tumor cells, and long-time chemotherapy reduces the sensitivity of tumor cells to chemotherapy drugs due to the presence of drug-resistant proteins on the cell membranes for drug outward transportation. Therefore, we reported a nano platform based on mesoporous silica coated with polydopamine (MSN@PDA) loading PDT enhancer MnO2, photosensitizer indocyanine green (ICG) and chemotherapeutic drug doxorubicin (DOX) (designated as DMPIM) to achieve a sequential release of different drugs to enhance treatment of malignant tumors. MSN was first synthesized by a template method, then DOX was loaded into the mesoporous channels of MSN, and locked by the PDA coating. Next, ICG was modified by π–π stacking on PDA, and finally, MnO2 layer was accumulated on the surface of DOX@MSN@PDA- ICG@MnO2, achieving orthogonal loading and sequential release of different drugs. DMPIM first generated oxygen (O2) through the reaction between MnO2 and H2O2 after entering tumor cells, alleviating the hypoxic environment of tumors and enhancing the PDT effect of sequentially released ICG. Afterwards, ICG reacted with O2 in tumor tissue to produce reactive oxygen species, promoting lysosomal escape of drugs and inactivation of p-glycoprotein (p-gp) on tumor cell membranes. DOX loaded in the MSN channels exhibited a delay of approximately 8 h after ICG release to exert the enhanced chemotherapy effect. The drug delivery system achieved effective sequential release and multimodal combination therapy, which achieved ideal therapeutic effects on malignant tumors. This work offers a route to a sequential drug release for advancing the treatment of malignant tumors.
Xiaoyu Lu et al 2024 Biomed. Mater. 19 045003
Artificial bone graft with osteoconductivity, angiogenesis, and immunomodulation is promising clinical therapeutics for the reluctant healing process of bone defects. Among various osteogenic substitutes, polymethyl methacrylate (PMMA) bone cement is a quit competitive platform due to its easy deployment to the bone defects with irregular shape and biomimetic mechanical properties. However, the biologically inert essence of PMMA is reliant on the passive osseointegration and cannot provide sufficient biologic cues to induce fast bone repair. Bioactive glass could serve as an efficient platform for the active osteogenesis of PMMA via ionic therapy and construction of alkaline microenvironment. However, the direct of deployment of bioactive glass into PMMA may trigger additional cytotoxicity and hinder cell growth on its surface. Hence we incorporated ionic therapy as osteogenic cue into the PMMA to enhance the biomedical properties. Specifically, we synthesized core-shell microspheres with a strontium-doped bioactive glass (SrBG) core and hydroxyapatite (HA) shell, and then composited them with PMMA to introduce multifunctional effects of HA incorporation, alkaline microenvironment construction, and functional ion release by adding microsphere. We prepared xSrBG@HA/PMMA cements (x = 30, 40, 50) with varied microsphere content and evaluated impacts on mechanical/handling properties, ion release, and investigated the impacts of different composite cements on proliferation, osteogenic differentiation, angiogenic potential, and macrophage polarization. These findings provide new perspectives and methodologies for developing advanced bone biomaterials to promote tissue regeneration.
Ananya Kashyap et al 2024 Biomed. Mater. 19 042001
In the biomedical industry, nanoparticles (NPs—exclusively small particles with size ranging from 1–100 nanometres) are recently employed as powerful tools due to their huge potential in sophisticated and enhanced cancer theragnostic (i.e. therapeutics and diagnostics). Cancer is a life-threatening disease caused by carcinogenic agents and mutation in cells, leading to uncontrolled cell growth and harming the body's normal functioning while affecting several factors like low levels of reactive oxygen species, hyperactive antiapoptotic mRNA expression, reduced proapoptotic mRNA expression, damaged DNA repair, and so on. NPs are extensively used in early cancer diagnosis and are functionalized to target receptors overexpressing cancer cells for effective cancer treatment. This review focuses explicitly on how NPs alone and combined with imaging techniques and advanced treatment techniques have been researched against 'women's cancer' such as breast, ovarian, and cervical cancer which are substantially occurring in women. NPs, in combination with numerous imaging techniques (like PET, SPECT, MRI, etc) have been widely explored for cancer imaging and understanding tumor characteristics. Moreover, NPs in combination with various advanced cancer therapeutics (like magnetic hyperthermia, pH responsiveness, photothermal therapy, etc), have been stated to be more targeted and effective therapeutic strategies with negligible side effects. Furthermore, this review will further help to improve treatment outcomes and patient quality of life based on the theragnostic application-based studies of NPs in women's cancer treatment.
Zhijun Zhang et al 2024 Biomed. Mater. 19 045002
The decellularized matrix has a great potential for tissue remodeling and regeneration; however, decellularization could induce host immune rejection due to incomplete cell removal or detergent residues, thereby posing significant challenges for its clinical application. Therefore, the selection of an appropriate detergent concentration, further optimization of tissue decellularization technique, increased of biosafety in decellularized tissues, and reduction of tissue damage during the decellularization procedures are pivotal issues that need to be investigated. In this study, we tested several conditions and determined that 0.1% Sodium dodecyl sulfate and three decellularization cycles were the optimal conditions for decellularization of pulp tissue. Decellularization efficiency was calculated and the preparation protocol for dental pulp decellularization matrix (DPDM) was further optimized. To characterize the optimized DPDM, the microstructure, odontogenesis-related protein and fiber content were evaluated. Our results showed that the properties of optimized DPDM were superior to those of the non-optimized matrix. We also performed the 4D-Label-free quantitative proteomic analysis of DPDM and demonstrated the preservation of proteins from the natural pulp. This study provides a optimized protocol for the potential application of DPDM in pulp regeneration.
Open all abstracts, in this tab
Ananya Kashyap et al 2024 Biomed. Mater. 19 042001
In the biomedical industry, nanoparticles (NPs—exclusively small particles with size ranging from 1–100 nanometres) are recently employed as powerful tools due to their huge potential in sophisticated and enhanced cancer theragnostic (i.e. therapeutics and diagnostics). Cancer is a life-threatening disease caused by carcinogenic agents and mutation in cells, leading to uncontrolled cell growth and harming the body's normal functioning while affecting several factors like low levels of reactive oxygen species, hyperactive antiapoptotic mRNA expression, reduced proapoptotic mRNA expression, damaged DNA repair, and so on. NPs are extensively used in early cancer diagnosis and are functionalized to target receptors overexpressing cancer cells for effective cancer treatment. This review focuses explicitly on how NPs alone and combined with imaging techniques and advanced treatment techniques have been researched against 'women's cancer' such as breast, ovarian, and cervical cancer which are substantially occurring in women. NPs, in combination with numerous imaging techniques (like PET, SPECT, MRI, etc) have been widely explored for cancer imaging and understanding tumor characteristics. Moreover, NPs in combination with various advanced cancer therapeutics (like magnetic hyperthermia, pH responsiveness, photothermal therapy, etc), have been stated to be more targeted and effective therapeutic strategies with negligible side effects. Furthermore, this review will further help to improve treatment outcomes and patient quality of life based on the theragnostic application-based studies of NPs in women's cancer treatment.
Zeqi Liu et al 2024 Biomed. Mater. 19 032005
Spinal cord injury (SCI) is a devastating neurological disorder, leading to loss of motor or somatosensory function, which is the most challenging worldwide medical problem. Re-establishment of intact neural circuits is the basis of spinal cord regeneration. Considering the crucial role of electrical signals in the nervous system, electroactive bioscaffolds have been widely developed for SCI repair. They can produce conductive pathways and a pro-regenerative microenvironment at the lesion site similar to that of the natural spinal cord, leading to neuronal regeneration and axonal growth, and functionally reactivating the damaged neural circuits. In this review, we first demonstrate the pathophysiological characteristics induced by SCI. Then, the crucial role of electrical signals in SCI repair is introduced. Based on a comprehensive analysis of these characteristics, recent advances in the electroactive bioscaffolds for SCI repair are summarized, focusing on both the conductive bioscaffolds and piezoelectric bioscaffolds, used independently or in combination with external electronic stimulation. Finally, thoughts on challenges and opportunities that may shape the future of bioscaffolds in SCI repair are concluded.
Ritu Raj et al 2024 Biomed. Mater. 19 032004
Electrospinning technique converts polymeric solutions into nanoscale fibers using an electric field and can be used for various biomedical and clinical applications. Extracellular vesicles (EVs) are cell-derived small lipid vesicles enriched with biological cargo (proteins and nucleic acids) potential therapeutic applications. In this review, we discuss extending the scope of electrospinning by incorporating stem cell-derived EVs, particularly exosomes, into nanofibers for their effective delivery to target tissues. The parameters used during the electrospinning of biopolymers limit the stability and functional properties of cellular products. However, with careful consideration of process requirements, these can significantly improve stability, leading to longevity, effectiveness, and sustained and localized release. Electrospun nanofibers are known to encapsulate or surface-adsorb biological payloads such as therapeutic EVs, proteins, enzymes, and nucleic acids. Small EVs, specifically exosomes, have recently attracted the attention of researchers working on regeneration and tissue engineering because of their broad distribution and enormous potential as therapeutic agents. This review focuses on current developments in nanofibers for delivering therapeutic cargo molecules, with a special emphasis on exosomes. It also suggests prospective approaches that can be adapted to safely combine these two nanoscale systems and exponentially enhance their benefits in tissue engineering, medical device coating, and drug delivery applications.
Tanima Dey et al 2024 Biomed. Mater. 19 032003
In terms of biomedical tools, nanodiamonds (ND) are a more recent innovation. Their size typically ranges between 4 to 100 nm. ND are produced via a variety of methods and are known for their physical toughness, durability, and chemical stability. Studies have revealed that surface modifications and functionalization have a significant influence on the optical and electrical properties of the nanomaterial. Consequently, surface functional groups of NDs have applications in a variety of domains, including drug administration, gene delivery, immunotherapy for cancer treatment, and bio-imaging to diagnose cancer. Additionally, their biocompatibility is a critical requisite for their in vivo and in vitro interventions. This review delves into these aspects and focuses on the recent advances in surface modification strategies of NDs for various biomedical applications surrounding cancer diagnosis and treatment. Furthermore, the prognosis of its clinical translation has also been discussed.
Wenjing Yin et al 2024 Biomed. Mater. 19 032002
Exosomes, typically 30–150 nm in size, are lipid-bilayered small-membrane vesicles originating in endosomes. Exosome biogenesis is regulated by the coordination of various mechanisms whereby different cargoes (e.g. proteins, nucleic acids, and lipids) are sorted into exosomes. These components endow exosomes with bioregulatory functions related to signal transmission and intercellular communication. Exosomes exhibit substantial potential as drug-delivery nanoplatforms owing to their excellent biocompatibility and low immunogenicity. Proteins, miRNA, siRNA, mRNA, and drugs have been successfully loaded into exosomes, and these exosome-based delivery systems show satisfactory therapeutic effects in different disease models. To enable targeted drug delivery, genetic engineering and chemical modification of the lipid bilayer of exosomes are performed. Stimuli-responsive delivery nanoplatforms designed with appropriate modifications based on various stimuli allow precise control of on-demand drug delivery and can be utilized in clinical treatment. In this review, we summarize the general properties, isolation methods, characterization, biological functions, and the potential role of exosomes in therapeutic delivery systems. Moreover, the effective combination of the intrinsic advantages of exosomes and advanced bioengineering, materials science, and clinical translational technologies are required to accelerate the development of exosome-based delivery nanoplatforms.
Open all abstracts, in this tab
Li et al
Supramolecular chemistry is versatile for developing stimuli-responsive, dynamic and multifunctional structures. In the context of biomedical engineering applications, supramolecular assemblies are particularly useful as coatings for they can closely mimic the natural structure and organisation of the extracellular matrix (ECM), they can also fabricate other complex systems like drug delivery systems and bioinks. In the current context of growing medical device-associated complications and the developments in the controlled drug delivery and regenerative medicine fields,supramolecular assemblies are becoming an indispensable part of the biomedical engineering arsenal. This review covers the different supramolecular assemblies in different biomedical applications with a specific focus on antimicrobial coatings, coatings that enhance biocompatibility, surface modifications on implantable medical devices, systems that promote therapeutic efficiency in cancer therapy, and the development in bioinks. The introduced supramolecularsystems include multilayer coating by polyelectrolytes, polymers incorporated with nanoparticles, coating simulation of ECM, and drug delivery systems. A perspective on the application of supramolecular systems is also included.
Yan et al
The sensitivity and diagnostic accuracy of magnetic resonance imaging (MRI) mainly depend on the relaxation capacity of contrast agents (CAs) and their accumulated amount at the pathological region. Due to the better biocompatibility and high-spin capacity, Fe-complexes have been studied widely as an alternative to replace popular Gd-based CAs associated with potential biotoxicity. Compared with a variety of Fe complex-based CAs, such as small molecular, macrocyclic, multinuclear complexes, the form of nanoparticle exhibits outstanding longitudinal relaxation, but the clinical transformation was still limited by the inconspicuous difference of contrast between tumor and normal tissue. The enhanced effect of contrast is a positive relation as relaxation of CAs and their concentration in desired region. To specifically improve the amount of CAs accumulated in the tumor, pH-responsive polymer poly(2-ethyl-2-oxazoline) (PEOz) was modified on melanin, a ubiquitous natural pigment providing much active sites for chelating with Fe(III). The Fe(III)-Mel-PEOz we prepared could raise the tumor cell endocytosis efficiency via switching surface charge from anion to cation with the stimuli of the decreasing pH of tumor microenvironment. The change of pH has negligible effect on the r1 of Fe(III)-Mel-PEOz, which is always maintained at around 1.0 mM-1s-1 at 0.5 T. Moreover, Fe(III)-Mel-PEOz exhibited low cytotoxicity, and satisfactory enhancement of positive contrast effect in vivo. The excellent biocompatibility and stable relaxation demonstrate the high potential of Fe(III)-Mel-PEOz in the diagnosis of tumor.
Yunoki et al
Bundles of engineered collagen microfibers are promising synthetic tendons as substitutes for autogenous grafts. The purpose of this study was to develop high-speed and continuous spinning of collagen microfibers that involves stretching of collagen stream. Our study revealed the "critical fibrillogenesis concentration (CFC)" of neutralized collagen solutions, which is defined as the upper limit of the collagen concentration at which neutralized collagen molecules remain stable as long as they are cooled (≤10°C). Neutralized collagen solutions at collagen concentrations slightly below the CFC formed cord-like collagen gels comprising longitudinally aligned fibrils when extruded from nozzles into an ethanol bath. Dry collagen microfibers with a controlled diameter ranging from 122 ± 2 to 31.2 ± 1.7 μm can be spun from the cord-like gels using nozzles of various sizes. The spinning process was improved by including stretching of collagen stream to further reduce diameter and increase linear velocity. We extruded a collagen solution through a 182-μm-diameter nozzle while simultaneously stretching it in an ethanol bath during gelation and fiber formation. This process resembles the stretching of a melted thermoplastic resin because it solidifies during melt spinning. The mechanical properties of the stretched collagen microfibers were comparable to the highest literature values obtained using microfluidic wet spinning, as they exhibited longitudinally aligned fibrils both on their surface and in their core. Previous wet spinning methods were unable to generate collagen microfibers with a consistent tendon-like fibrillar arrangement throughout the samples. Although the tangent modulus (101 ± 16 MPa) and stress at break of the swollen bundles of stretched microfibers (10.5 ± 0.5 MPa) were lower than those of ACL, they were within the same order of magnitude. We developed a spinning technique that produces narrow collagen microfibers with a tendon-like arrangement that can serve as artificial fiber units for collagen-based synthetic tendons.
Yang et al
In this study, we coated electrospun polycaprolactone (PCL) fibers with polydopamine (PDA) to modify their hydrophobicity and fabricated a matrix for culturing mesenchymal stem cells (MSCs). Additionally, we incorporated Arg-Gly-Asp (RGD) peptides into PDA to enhance MSCs culture performance on PCL fibers. PDA and RGD were successfully coated in one step by immersing the electrospun fibers in a coating solution, without requiring an additional surface activation process. The characteristics of functionalized PCL fibers were analyzed by scanning electron microscope (SEM) with energy-dispersive X-ray (EDX) analysis, Fourier transform infrared (FTIR) spectroscopy, water contact angle measurement, and fluorescence measurements using a carboxylic-modified fluorescent microsphere. MSCs cultured on the modified PCL fibers demonstrated enhanced cell adhesion, proliferation, and osteogenic- and chondrogenic differentiation. This study provides insight into potential applications for scaffold fabrication in MSCs-based tissue engineering, wound dressing, implantation, and a deeper understanding of MSCs behavior in vitro.
Li et al
To effectively address underlying issues and enhance the healing process of hard-to-treat soft tissue defects, innovative therapeutic approaches are required. One promising strategy involves the incorporation of bioactive substances into biodegradable scaffolds to facilitate synergistic tissue regeneration, particularly in vascular regeneration. In this study, we introduce a composite hydrogel design that mimics the extracellular matrix (ECM) by covalently combining gelatin and hyaluronic acid (HA), with the encapsulation of deferoxamine nanoparticles (DFO NPs) for potential tissue regeneration applications. Crosslinked hydrogels were fabricated by controlling the ratio of HA in the gelatin-based hydrogels, resulting in improved mechanical properties, enhanced degradation ability, and optimised porosity, compared with hydrogel formed by gelatin alone. The DFO NPs, synthesized using a double emulsion method with PLGA, exhibited a sustained release of DFO over 12 days. Encapsulating the DFO NPs in the hydrogel enabled controlled release over 15 days. The DFO NPs, composite hydrogel, and the DFO NPs loaded hydrogel exhibited excellent cytocompatibility and promoted cell proliferation in vitro. Subcutaneous implantation of the composite hydrogel and the DFO NPs loaded hydrogel demonstrated biodegradability, tissue integration, and no obvious adverse effects, evidenced by histological analysis. Furthermore, the DFO NPs loaded composite hydrogel exhibited accelerated wound closure and promoted neovascularisation and granular formation when tested in an excisional skin wound model in mice. These findings highlight the potential of our composite hydrogel system for promoting the faster healing of diabetes-induced skin wounds and oral lesions through its ability to modulate tissue regeneration processes.
Open all abstracts, in this tab
Zhijun Zhang et al 2024 Biomed. Mater. 19 045002
The decellularized matrix has a great potential for tissue remodeling and regeneration; however, decellularization could induce host immune rejection due to incomplete cell removal or detergent residues, thereby posing significant challenges for its clinical application. Therefore, the selection of an appropriate detergent concentration, further optimization of tissue decellularization technique, increased of biosafety in decellularized tissues, and reduction of tissue damage during the decellularization procedures are pivotal issues that need to be investigated. In this study, we tested several conditions and determined that 0.1% Sodium dodecyl sulfate and three decellularization cycles were the optimal conditions for decellularization of pulp tissue. Decellularization efficiency was calculated and the preparation protocol for dental pulp decellularization matrix (DPDM) was further optimized. To characterize the optimized DPDM, the microstructure, odontogenesis-related protein and fiber content were evaluated. Our results showed that the properties of optimized DPDM were superior to those of the non-optimized matrix. We also performed the 4D-Label-free quantitative proteomic analysis of DPDM and demonstrated the preservation of proteins from the natural pulp. This study provides a optimized protocol for the potential application of DPDM in pulp regeneration.
Haiyu Yu et al 2024 Biomed. Mater.
Porous tantalum scaffolds offer a high degree of biocompatibility and have a low friction coefficient. In addition, their biomimetic porous structure and mechanical properties, which closely resemble human bone tissue, make them a popular area of research in the field of bone defect repair. With the rapid advancement of additive manufacturing, 3D-printed porous tantalum scaffolds have increasingly emerged in recent years, offering exceptional design flexibility, as well as facilitating the fabrication of intricate geometries and complex pore structures that similar to human anatomy. This review provides a comprehensive description of the techniques, procedures, and specific parameters involved in the 3D printing of porous tantalum scaffolds. Concurrently, the review provides a summary of the mechanical properties, osteogenesis and antibacterial properties of porous tantalum scaffolds. The use of surface modification techniques and the drug carriers can enhance the characteristics of porous tantalum scaffolds. Accordingly, the review discusses the application of these porous tantalum materials in clinical settings. Multiple studies have demonstrated that 3D-printed porous tantalum scaffolds exhibit exceptional corrosion resistance, biocompatibility, and osteogenic properties. As a result, they are considered highly suitable biomaterials for repairing bone defects. Despite the rapid development of 3D-printed porous tantalum scaffolds, they still encounter challenges and issues when used as bone defect implants in clinical applications. Ultimately, a concise overview of the primary challenges faced by 3D-printed porous tantalum scaffolds is offered, and corresponding insights to promote further exploration and advancement in this domain are presented.
Xiaoming Liu et al 2024 Biomed. Mater.
In the field of medicine, we often brave the unknown like interstellar explorers, especially when confronting the formidable opponent of hepatocellular carcinoma (HCC). The global burden of HCC remains significant, with suboptimal treatment outcomes necessitating the urgent development of novel drugs and treatments. While various treatments for liver cancer, such as immunotherapy and targeted therapy, have emerged in recent years, improving their transport and therapeutic efficiency, controlling their targeting and release, and mitigating their adverse effects remains challenging. However, just as we grope through the darkness, a glimmer of light emerges - nanotechnology. Recently, nanotechnology has attracted attention because it can increase the local drug concentration in tumors, reduce systemic toxicity, and has the potential to enhance the effectiveness of precision therapy for HCC. However, there are also some challenges hindering the clinical translation of drug-loaded nanoparticles (NPs). Just as interstellar explorers must overcome interstellar dust, we too must overcome various obstacles. In future researches, the design and development of nanodelivery systems for novel drugs treating HCC should be the first attention. Moreover, researchers should focus on the active targeting design of various NPs. The combination of the interventional therapies and drug-loaded NPs will greatly advance the process of precision HCC therapy.
Laura Rodríguez-Mandujano et al 2024 Biomed. Mater.
Collagen type I is a material widely used for 3D cell culture and tissue engineering. Different architectures, such as gels, sponges, membranes, and nanofibers, can be fabricated with it. In collagen hydrogels, the formation of fibrils and fibers depends on various parameters, such as the source of collagen, pH, temperature, concentration, age, etc. In this work, we study the fibrillogenesis process in collagen type I hydrogels with different types of microbeads embedded, using optical techniques such as turbidity assay and confocal reflectance microscopy. We observe that microbeads embedded in the collagen matrix hydrogels modify the fibrillogenesis. Our results show that carboxylated fluorescent microbeads accelerate 3.6 times the gelation, while silica microbeads slow down the formation of collagen fibrils by a factor of 1.9, both compared to pure collagen hydrogels. Our observations suggest that carboxylate microbeads act as nucleation sites and the early collagen fibrils bind to the microbeads.
Eliza Ranjit et al 2024 Biomed. Mater. 19 035036
Wool derived keratin, due to its demonstrated ability to promote bone formation, has been suggested as a potential bioactive material for implant surfaces. The aim of this study was to assess the effects of keratin-coated titanium on osteoblast function in vitro and bone healing in vivo. Keratin-coated titanium surfaces were fabricated via solvent casting and molecular grafting. The effect of these surfaces on the attachment, osteogenic gene, and osteogenic protein expression of MG-63 osteoblast-like cells were quantified in vitro. The effect of these keratin-modified surfaces on bone healing over three weeks using an intraosseous calvaria defect was assessed in rodents. Keratin coating did not affect MG-63 proliferation or viability, but enhanced osteopontin, osteocalcin and bone morphogenetic expression in vitro. Histological analysis of recovered calvaria specimens showed osseous defects covered with keratin-coated titanium had a higher percentage of new bone area two weeks after implantation compared to that in defects covered with titanium alone. The keratin-coated surfaces were biocompatible and stimulated osteogenic expression in adherent MG-63 osteoblasts. Furthermore, a pilot preclinical study in rodents suggested keratin may stimulate earlier intraosseous calvaria bone healing.
Zhihui Chen et al 2024 Biomed. Mater.
Cervical carcinoma persists as a major global public health burden. While conventional therapeutic modalities inevitably cause ablation of adjacent non-tumorous tissues, photodynamic therapy (PDT) offers a targeted cytotoxic strategy through a photosensitizing agent (PS). However, the hydrophobicity and lack of selective accumulation of promising PS compounds such as zinc(II) phthalocyanine (ZnPc) impedes their clinical translation as standalone agents. The present study sought to incorporate ZnPc within double-layer hollow mesoporous silica nanoparticles (DHMSN) as nanocarriers to enhance aqueous dispersibility and tumor specificity. Owing to their compartmentalized design, the hollow mesoporous silica nanoparticles (HMSN) demonstrated enhanced ultrasonic imaging contrast. Combined with the vaporization of the perfluorocarbon perfluoropentane (PFP), the HMSN-encapsulated ZnPc enabled real-time ultrasound monitoring of PDT treatment. In vivo, the innate thermal energy induced vaporization of the DHMSN-carried PFP to significantly amplify ultrasound signals from the tumor site. Results demonstrated biocompatibility, efficient PFP microbubble generation, and robust photocatalytic activity. Collectively, this investigation establishes ultrasound-guided PDT utilizing multi-layer HMSN as a targeted therapeutic strategy for cervical malignancies with mitigated toxicity.
Chang Liu et al 2024 Biomed. Mater. 19 035028
In bone tissue engineering, the bone immunomodulatory properties of biomaterials are critical for bone regeneration, which is a synergistic process involving physiological activities like immune response, osteogenesis, and angiogenesis. The effect of the macrophage immune microenvironment on the osteogenesis and angiogenesis of various material extracts was examined in this experiment using Mg2+ and Nano-hydroxyapatite/collagen (nHAC) in both a single application and a combined form. This study in vitro revealed that the two compounds combined significantly inhibited the NF-κB signaling pathway and reduced the release of inflammatory factors from macrophages when compared with the extraction phase alone. Additionally, by contributing to the polarization of macrophages towards the M2 type, the combined effects of the two materials can significantly improve osteogenesis/angiogenesis. The results of in vivo experiments confirmed that Mg2+/nHAC significantly promoted bone regeneration and angiogenesis. This study offers a promising method for enhancing bone graft material osseointegration.
Aysel Koç-Demir et al 2024 Biomed. Mater. 19 035027
The development of new three-dimensional biomaterials with advanced versatile properties is critical to the success of tissue engineering (TE) applications. Here, (a) bioactive decellularized tendon extracellular matrix (dECM) with a sol-gel transition feature at physiological temperature, (b) halloysite nanotubes (HNT) with known mechanical properties and bioactivity, and (c) magnetic nanoparticles (MNP) with superparamagnetic and osteogenic properties were combined to develop a new scaffold that could be used in prospective bone TE applications. Deposition of MNPs on HNTs resulted in magnetic nanostructures without agglomeration of MNPs. A completely cell-free, collagen- and glycosaminoglycan- rich dECM was obtained and characterized. dECM-based scaffolds incorporated with 1%, 2% and 4% MNP-HNT were analysed for their physical, chemical, and in vitro biological properties. Fourier-transform infrared spectroscopy, x-ray powder diffractometry and vibrating sample magnetometry analyses confirmed the presence of dECM, HNT and MNP in all scaffold types. The capacity to form apatite layer upon incubation in simulated body fluid revealed that dECM-MNP-HNT is a bioactive material. Combining dECM with MNP-HNT improved the thermal stability and compressive strength of the macroporous scaffolds upto 2% MNP-HNT. In vitro cytotoxicity and hemolysis experiments showed that the scaffolds were essentially biocompatible. Human bone marrow mesenchymal stem cells adhered and proliferated well on the macroporous constructs containing 1% and 2% MNP-HNT; and remained metabolically active for at least 21 d in vitro. Collectively, the findings support the idea that magnetic nanocomposite dECM scaffolds containing MNP-HNT could be a potential template for TE applications.
Sophie Schweinitzer et al 2024 Biomed. Mater. 19 031001
Tissue-like constructs, intended for application in tissue engineering and regenerative medicine, can be produced by three-dimensional (3D) bioprinting of cells in hydrogels. It is essential that the viability and proliferation of the encapsulated cells can be reliably determined. Methods currently used to evaluate cell proliferation, such as quantification of DNA and measurement of metabolic activity, have been developed for application in 2D cultures and might not be suitable for bioinks. In this study, human fibroblasts were either cast or printed in gelatin methacryloyl (GelMA) or sodium alginate hydrogels and cell proliferation was assessed by AlamarBlue, PicoGreen and visual cell counts. Comparison of data extrapolated from standard curves generated from 2D cultures and 3D hydrogels showed potential inaccuracies. Moreover, there were pronounced discrepancies in cell numbers obtained from these assays; the different bioinks strongly influenced the outcomes. Overall, the results indicate that more than one method should be applied for better assessment of cell proliferation in bioinks.
Alexandra Jednorski et al 2024 Biomed. Mater. 19 035022
Cd0.3Pb0.7S (CdPbS) aqueous quantum dots (AQDs) made with 3-mercaptoproprionic acid (MPA) as a ligand have the advantages of emitting near-infrared light, well above 800 nm, that completely circumvents interference from tissue autofluorescence and have significant amounts of ligands for bioconjugation. However, retaining the right amount of MPA became a challenge when using CdPbS AQDs for bioimaging because retaining too much MPA could lead to significant nonspecific staining in cell imaging while insufficient MPA could cause AQDs instability in biological systems. Here we examined PEGylation (i.e. chemically linking amine-functionalized polyethylene glycol (PEG)) to modify MPA on the AQDs surface to improve AQDs stability and reduce nonspecific staining. In addition, for conjugation with antibodies, a bifunctional PEG with a carboxyl functionality was used to permit chemical linkage of a PEG to an antibody on the other end. It was found that performing PEGylation at the thiol concentration where the zeta potential becomes saturated stabilized the CdPbS AQDs suspension and reduced nonspecific binding to cells. Furthermore, with the bifunctional PEG, the CdPbS AQDs were conjugated with antibodies and the AQD-Ab conjugates were shown to stain cancer cells specifically against normal cells with a signal-to-noise ratio of 8.